Sandell’s Control Joint Gaskets are manufactured to be used
with standard sash block to allow for expansion and contraction
of masonry walls. Test data and results set forth herein are
based on laboratory work under controlled conditions and do
not necessarily indicate the result that the buyer or user will
attain.
| SANDELL®’S
2010 RUBBER CONTROL JOINT
Sandell®’s 2010 Rubber Control Joint is manufactured from a
high grade synthetic rubber
compound. It has a durometer hardness of 80 shore A when tested in with
ASTM
D-2240.
Physical properties for Sandell’s 2010 Rubber Control Joint are
as follows: |
PROPERTY |
NOMINAL VALUE |
TEST METHOD |
Tensile strength |
1260 PSI |
ASTM D-412 |
Ultimate Elongation |
360% |
ASTM D-412 |
Low Temp. Brittleness |
-62°F |
ASTM D-746 |
Compression Set @ 77°F |
30% |
ASTM D-395, Method B |
|
SANDELL®’S
2011 PVC CONTROL JOINT
Sandell®’s 2011 PVC Control Joint is manufactured from a flexible
PVC compound, conforming to ASTM D-2240-554. This product is in compliance
with a durometer hardness of 80 + 5 shore A, when tested in conventional
ASTM D-2240 methods.
Physical properties for Sandell’s 2011 PVC Control Joint are as
follows: |
PROPERTY |
NOMINAL VALUE |
TEST METHOD |
Tensile strength |
1750 PSI |
ASTM D-638 |
Ultimate Elongation |
300% |
ASTM D-638 |
Density |
1.35 |
ASTM D-297 |
|
SANDELL®’S
2012 RUBBER CONTROL JOINT
Sandell®’s 2012 Rubber Control Joint is manufactured from a high
grade synthetic rubber compound. It has a durometer hardness of 80 shore
A when tested in conventional ASTM D-2240 test methods. |
|
SANDELL®’S
2012 - PVC CONTROL JOINT
Sandell®’s 2012 - PVC Control Joint is manufactured from a flexible
PVC compound, conforming to ASTM D-2287-654. This product is in compliance
with a durometer hardness of 80 + 5 shore A, when tested in conventional
ASTM D-2240 test methods.
Physical properties for Sandell’s 2012 PVC Control Joint is as
follows: |
PROPERTY |
NOMINAL VALUE |
TEST METHOD |
Tensile strength |
1750 PSI |
ASTM D-638 |
Ultimate Elongation |
300% |
ASTM D-638 |
Density |
1.39 |
ASTM D-297 |
|
SANDELL®’S
2013 RUBBER CONTROL JOINT
Sandell®’s 2013 Rubber Control Joint is manufactured from a high
grade synthetic rubber compound with a durometer hardness of 80 shore
A when tested in conventional ASTM D-2240 test methods. |
|
SANDELL®’S
2013 - PVC CONTROL JOINT
Sandell®’s 2013 - PVC Control Joint is manufactured from a flexible
PVC compound, conforming to ASTM D-2287-654. This product is in compliance
with a durometer hardness of 80 + 5 shore A, when tested in conventional
ASTM D-2240 tests methods.
Physical properties for Sandell’s 2013 PVC Control Joint is as
follows: |
PROPERTY |
NOMINAL VALUE |
TEST METHOD |
Tensile strength |
1750 PSI |
ASTM D-638 |
Ultimate Elongation |
300% |
ASTM D-638 |
Density |
1.39 |
ASTM D-297 |
|
SANDELL®’S
2014 TEE RUBBER CONTROL JOINT
Sandell®’s 2014 Tee Rubber Control Joint is manufactured from a
high grade synthetic rubber compound. It has a durometer hardness of 80
shore A when tested in with ASTM D-2240. |
|
SANDELL®’S
2014 TEE - PVC CONTROL JOINT
Sandell®’s 2014 Tee - PVC Control Joint is manufactured from a
flexible PVC compound, conforming to ASTM D-2240-554. This product is
in compliance with a durometer hardness of 80 + 5 shore A, when tested
in conventional ASTM D-2240 methods.
Physical properties for Sandell’s 2014 Tee-PVC Control Joint are
as follows: |
PROPERTY |
NOMINAL VALUE |
TEST METHOD |
Tensile strength |
1750 PSI |
ASTM D-638 |
Ultimate Elongation |
300% |
ASTM D-638 |
Density |
1.35 |
ASTM D-297 |